牌号 cw509l 易切削黄铜

对应标准 din en 1652:-1986

铜及铜合金棒及型材(锻件除外)

copper***copper alloy rods***sections (other than forging stock)

归类 铜及铜合金

标签 易切削铅黄铜

用途：锻铜合金；铜锌合金（黄铜）；（特殊黄铜）；化学成分。

热处理：1274°c-1232°c。

en cw509l en 1652:

element min max similar

ni - 0.3 -

cu 59 61.5 -

al - 0.05 -

zn - - -

sn - 0.2 -

fe - 0.2 -

pb - 0.2 -

others total - 0.2 -

total others - 0.2 -

en cw509l en 1652 mechanical

yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)

rp0.2 (mpa) rm (mpa) kv/ku (j) a (％) z (％)

833 (≥) 376 (≥) 41 42 24 solution***aging, annealing, ausaging, q+t,etc 331

en cw509l en 1652 physical

the en cw509l en 1652 material physical properties shall comply with the values given in the following table.

temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν

(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)

44 - - 0.12 -

548 722 - 14.3 143 -

883 - 43 21.2 211 222

en cw509l en 1652 processing service

cw509l是一种以铜为基础的合金材料,通过添加铅、铁、硅等元素 ,使其具有优良的切削性能。这种合金被广泛用于机械制造、电子、建筑等领域,因其易切削性、耐腐蚀性和高导电性而受到青睐。

在cw509l合金中,铅是最主要的添加元素 ,含量高达3.5％~4.5％。铅在合金中的主要作用是提高切削性能,同时还能改善合金的耐磨性和延展性。此外,铁和硅也是该合金的重要添加元素 ,它们的加入进一步增强了合金的强度和硬度,提高了耐腐蚀性能。

cw509l合金的物理性质方面,其密度约为8.5g/cm3,具有高导电性和良好的热导率。此外,该合金还具有优良的冷加工性能,可通过轧制、挤压、拉伸等工艺制作成各种复杂形状的零件。

在化学性质方面,cw509l合金具有良好的耐腐蚀性,尤其是对弱酸 和盐 类物质的耐腐蚀性较好。然而,由于铅的存在,该合金不建议在食品或医 药等领域使用。

总的来说,cw509l易切削黄铜是一种具有广泛用途的金属材料,其优良的切削性能、耐腐蚀性和高导电性使其在机械制造、电子、建筑等领域得到广泛应用