dupont performance polymers zytel® 7335f nc010 nylon 6 (unverified data**) 物性表 物理性能 额定值 (公制) 额定值 (英制) 测试方法

密度	1.13 g/cc	0.0408 lb/in3	dam; iso 1183
water absorption	3.0 ％ @temperature 23.0 °c	3.0 ％ @temperature 73.4 °f	equilibrium 50％rh; dam; iso 62, similar to
	9.0 ％ @temperature 23.0 °c	9.0 ％ @temperature 73.4 °f	saturation, immersed; dam; iso 62, similar to
线性成型收缩率	0.0075 cm/cm @thickness 1.60 mm	0.0075 in/in @thickness 0.0630 in	dam
	0.010 cm/cm @thickness 3.20 mm	0.010 in/in @thickness 0.126 in	dam
线性成型收缩率,flow	0.0060 cm/cm @thickness 2.00 mm	0.0060 in/in @thickness 0.0787 in	dam; iso 294-4
线性成型收缩率，横向	0.0080 cm/cm @thickness 2.00 mm	0.0080 in/in @thickness 0.0787 in	dam; iso 294-4

机械性能 额定值 (公制) 额定值 (英制) 测试方法

抗张强度(屈服)	55.0 mpa @temperature 23.0 °c	7980 psi @temperature 73.4 °f	50％rh; iso 527
	90.0 mpa @temperature 23.0 °c	13100 psi @temperature 73.4 °f	dam; iso 527
伸长率 (断裂)	9.0 ％ @temperature 23.0 °c	9.0 ％ @temperature 73.4 °f	dam; nominal; iso 527
	15 ％ @temperature 23.0 °c	15 ％ @temperature 73.4 °f	50mm/min; dam; iso 527
	>= 50 ％ @temperature 23.0 °c	>= 50 ％ @temperature 73.4 °f	50mm/min; 50％rh; iso 527
	>= 50 ％ @temperature 23.0 °c	>= 50 ％ @temperature 73.4 °f	50％rh; nominal; iso 527
elongation at yield	3.8 ％ @temperature 23.0 °c	3.8 ％ @temperature 73.4 °f	dam; iso 527
	24 ％ @temperature 23.0 °c	24 ％ @temperature 73.4 °f	50％rh; iso 527
拉伸模量	1.40 gpa @temperature 23.0 °c	203 ksi @temperature 73.4 °f	50％rh; iso 527
	3.60 gpa @temperature 23.0 °c	522 ksi @temperature 73.4 °f	dam; iso 527
简支梁无缺口冲击强度	6.00 j/cm2 @temperature -30.0 °c	28.6 ft-lb/in2 @temperature -22.0 °f	50％rh; iso 179/1eu
	7.00 j/cm2 @temperature 23.0 °c	33.3 ft-lb/in2 @temperature 73.4 °f	dam; iso 179/1eu
	11.0 j/cm2 @temperature -30.0 °c	52.3 ft-lb/in2 @temperature -22.0 °f	dam; iso 179/1eu
	12.0 j/cm2 @temperature 23.0 °c	57.1 ft-lb/in2 @temperature 73.4 °f	50％rh; iso 179/1eu
简支梁缺口冲击强度	0.250 j/cm2 @temperature -30.0 °c	1.19 ft-lb/in2 @temperature -22.0 °f	dam; iso 179/1ea
	0.300 j/cm2 @temperature -30.0 °c	1.43 ft-lb/in2 @temperature -22.0 °f	50％rh; iso 179/1ea
	0.450 j/cm2 @temperature 23.0 °c	2.14 ft-lb/in2 @temperature 73.4 °f	dam; iso 179/1ea
	1.80 j/cm2 @temperature 23.0 °c	8.57 ft-lb/in2 @temperature 73.4 °f	50％rh; iso 179/1ea

电气性能 额定值 (公制) 额定值 (英制) 测试方法

体积电阻率	1.00e+11 ohm-cm @temperature 23.0 °c	1.00e+11 ohm-cm @temperature 73.4 °f	50％rh; astm d257
	1.00e+11 ohm-cm @temperature 23.0 °c	1.00e+11 ohm-cm @temperature 73.4 °f	50％rh; iec 60093
	>= 1.00e+15 ohm-cm @temperature 23.0 °c	>= 1.00e+15 ohm-cm @temperature 73.4 °f	dam; iec 60093
	1.00e+17 ohm-cm @temperature 23.0 °c	1.00e+17 ohm-cm @temperature 73.4 °f	dam; astm d257
	1.00e+17 ohm-cm @temperature 23.0 °c	1.00e+17 ohm-cm @temperature 73.4 °f	dam; iec 60093
surface resistance	1.00e+11 ohm @temperature 23.0 °c	1.00e+11 ohm @temperature 73.4 °f	50％rh; astm d257
	1.00e+11 ohm @temperature 23.0 °c	1.00e+11 ohm @temperature 73.4 °f	50％rh; iec 60093
	1.00e+13 ohm @temperature 23.0 °c	1.00e+13 ohm @temperature 73.4 °f	dam; astm d257
介电常数	3.3 @frequency 1.00e+6 hz, temperature 23.0 °c	3.3 @frequency 1.00e+6 hz, temperature 73.4 °f	dam; astm d150
	3.6 @frequency 100 hz, temperature 23.0 °c	3.6 @frequency 100 hz, temperature 73.4 °f	dam; astm d150
	3.6 @frequency 1000 hz, temperature 23.0 °c	3.6 @frequency 1000 hz, temperature 73.4 °f	dam; astm d150
	4.2 @frequency 100 hz, temperature 23.0 °c	4.2 @frequency 100 hz, temperature 73.4 °f	dam; iec 60250
介电强度	13.5 kv/mm @thickness 3.20 mm, temperature 23.0 °c	343 kv/in @thickness 0.126 in, temperature 73.4 °f	50％rh; short time; astm d149
	16.3 kv/mm @thickness 3.20 mm, temperature 23.0 °c	414 kv/in @thickness 0.126 in, temperature 73.4 °f	dam; short time; astm d149
耗散因数	0.010 @frequency 1000 hz, temperature 23.0 °c	0.010 @frequency 1000 hz, temperature 73.4 °f	dam; astm d150
	0.010 @frequency 100 hz, temperature 23.0 °c	0.010 @frequency 100 hz, temperature 73.4 °f	dam; astm d150
	0.020 @frequency 1.00e+6 hz, temperature 23.0 °c	0.020 @frequency 1.00e+6 hz, temperature 73.4 °f	dam; astm d150
	0.030 @frequency 100 hz, temperature 23.0 °c	0.030 @frequency 100 hz, temperature 73.4 °f	dam; iec 60250
	0.11 @frequency 1.00e+6 hz, temperature 23.0 °c	0.11 @frequency 1.00e+6 hz, temperature 73.4 °f	50％rh; astm d150
	0.23 @frequency 1000 hz, temperature 23.0 °c	0.23 @frequency 1000 hz, temperature 73.4 °f	50％rh; astm d150
	0.37 @frequency 100 hz, temperature 23.0 °c	0.37 @frequency 100 hz, temperature 73.4 °f	50％rh; astm d150
相比耐漏电起痕指数(cti)	600 v @temperature 23.0 °c	600 v @temperature 73.4 °f	dam; iec 60112

热性能 额定值 (公制) 额定值 (英制) 测试方法

线形热膨胀系数 - 流动	500 μm/m-°c @temperature 23.0 - 55.0 °c	278 μin/in-°f @temperature 73.4 - 131 °f	dam; astm e 831
	500 μm/m-°c @temperature 23.0 - 55.0 °c	278 μin/in-°f @temperature 73.4 - 131 °f	dam; iso 11359-1/-2
线性热膨胀系数,横向流动	92.0 μm/m-°c @temperature 23.0 - 55.0 °c	51.1 μin/in-°f @temperature 73.4 - 131 °f	dam; astm e 831
	92.0 μm/m-°c @temperature 23.0 - 55.0 °c	51.1 μin/in-°f @temperature 73.4 - 131 °f	dam; iso 11359-1/-2
熔融温度	221 °c	430 °f	10°c/min; dam; iso 11357-1/-3
载荷下热变形温度(0.46 mpa)	175 °c	347 °f	dam; iso 75-1/-2
载荷下热变形温度(1.8 mpa)	65.0 °c	149 °f	dam; iso 75-1/-2
可燃性(ul94)	hb @thickness 1.50 mm	hb @thickness 0.0591 in	dam; ul94
	hb @thickness 1.50 mm	hb @thickness 0.0591 in	dam; iec 60695-11-10

加工性能 额定值 (公制) 额定值 (英制) 测试方法

加工（熔体）温度	260 - 280 °c	500 - 536 °f	dam
	270 °c	518 °f	dam; optimum
模具温度	70.0 °c	158 °f	dam; optimum
	50.0 - 90.0 °c	122 - 194 °f	dam
干燥温度	80.0 °c	176 °f	dam
干燥时间	2.00 - 4.00 hour	2.00 - 4.00 hour	dam
水分含量	<= 0.20 ％	<= 0.20 ％	dam

材料描述